dc.description.abstractThis paper explores the possibility of synthesising catalyst supports with improved properties. Alumina foams were produced with the polymer replication technique. Representative high- and low-temperature sintering ceramics were selected. Suitable suspension amounts, the clay addition and sintering temperature were determined. A lower sintering temperature was used for an economic enhancement of the process. The sintering was conducted at the temperatures from 1573 K to 1773 K for 60 min. A comparative analysis of the studied systems shows that the best compressive strength of 6.2 MPa was achieved with the system based on the alpha-Al2O3-25 clay (mass fractions, w/%), polyester foam with 10 PPI, sintered at 1673 K.en
dc.publisherInst Za Kovinske Materiale I In Tehnologie, Ljubjana
dc.relationinfo:eu-repo/grantAgreement/MESTD/Technological Development (TD or TR)/34033/RS//
dc.relationinfo:eu-repo/grantAgreement/MESTD/Technological Development (TD or TR)/34023/RS//
dc.rightsopenAccess
dc.sourceMaterials and Technology = Materiali in Tehnologije
dc.subjectaluminaen
dc.subjectreticulated foamen
dc.subjectsinteringen
dc.subjectmechanical propertiesen
dc.subjectcatalyst carrieren
dc.titleSynthesis of Alpha-Al2o3 Based Foams with Improved Properties as Catalyst Carriersen
dc.typearticle
dc.rights.licenseBY-NC
dcterms.abstractAнђић, Зоран; Сокиц, Мирослав; Корац, Марија; Камберовиц, Зељко; Николиц, Весна;
dc.citation.volume48
dc.citation.issue1
dc.citation.spage45
dc.citation.epage50
dc.identifier.wos000331494300008
dc.citation.other48(1): 45-50
dc.citation.rankM23
dc.type.versionpublishedVersion
dc.identifier.scopus2-s2.0-84894057926
dc.identifier.rcubKon_2625


Документи

Thumbnail

Овај рад се појављује у следећим колекцијама

Приказ основних података о документу