TY  - JOUR
AU  - Nikolić, Aleksandar S.
AU  - Cvetkovic, N
AU  - Djuric, S
AU  - Puzovic, J
AU  - Pavlović, Miodrag B.
PY  - 1998
UR  - https://cherry.chem.bg.ac.rs/handle/123456789/383
AB  - The conditions for the synthesis of ultra fine Ni-ferrites powder were investigated. The basic components were Fe(III) and Ni(II) complex compounds with acetylacetonato- (2,4 pentadione) ligands. Nanometrics powders were obtained by annealing the homogeneous mixture of the basic components in protected nitrogen atmosphere at different temperatures. The annealing temperature varied from 100 to 700 degrees C and the heating rate was 10 degrees C/min. The temperature effects on the composition and particles size of Ni-ferrites powders synthesized at 300, 400, 500 and 600 degrees C were investigated using X-ray analysis and transmission electron microscopy. Nanometrics Ni-ferrites powder was produced with less then 20 nm average particles size at 500 degrees C.
PB  - Transtec Publications Ltd, Zurich-Uetikon
T2  - Materials Science Forum
T1  - Temperature influence on the composition of Ni-ferrite powders obtained from complex compounds with acetylacetonato-ligands
SP  - 199
EP  - 202
DO  - 10.4028/www.scientific.net/MSF.282-283.199
ER  - 

@article{
author = "Nikolić, Aleksandar S. and Cvetkovic, N and Djuric, S and Puzovic, J and Pavlović, Miodrag B.",
year = "1998",
abstract = "The conditions for the synthesis of ultra fine Ni-ferrites powder were investigated. The basic components were Fe(III) and Ni(II) complex compounds with acetylacetonato- (2,4 pentadione) ligands. Nanometrics powders were obtained by annealing the homogeneous mixture of the basic components in protected nitrogen atmosphere at different temperatures. The annealing temperature varied from 100 to 700 degrees C and the heating rate was 10 degrees C/min. The temperature effects on the composition and particles size of Ni-ferrites powders synthesized at 300, 400, 500 and 600 degrees C were investigated using X-ray analysis and transmission electron microscopy. Nanometrics Ni-ferrites powder was produced with less then 20 nm average particles size at 500 degrees C.",
publisher = "Transtec Publications Ltd, Zurich-Uetikon",
journal = "Materials Science Forum",
title = "Temperature influence on the composition of Ni-ferrite powders obtained from complex compounds with acetylacetonato-ligands",
pages = "199-202",
doi = "10.4028/www.scientific.net/MSF.282-283.199"
}

Nikolić, A. S., Cvetkovic, N., Djuric, S., Puzovic, J.,& Pavlović, M. B.. (1998). Temperature influence on the composition of Ni-ferrite powders obtained from complex compounds with acetylacetonato-ligands. in Materials Science Forum
Transtec Publications Ltd, Zurich-Uetikon., 199-202.
https://doi.org/10.4028/www.scientific.net/MSF.282-283.199

Nikolić AS, Cvetkovic N, Djuric S, Puzovic J, Pavlović MB. Temperature influence on the composition of Ni-ferrite powders obtained from complex compounds with acetylacetonato-ligands. in Materials Science Forum. 1998;:199-202.
doi:10.4028/www.scientific.net/MSF.282-283.199 .

Nikolić, Aleksandar S., Cvetkovic, N, Djuric, S, Puzovic, J, Pavlović, Miodrag B., "Temperature influence on the composition of Ni-ferrite powders obtained from complex compounds with acetylacetonato-ligands" in Materials Science Forum (1998):199-202,
https://doi.org/10.4028/www.scientific.net/MSF.282-283.199 . .