AB  - In this investigation, samples of SrGd2O4 doped with different Yb3+ (2, 4, 6 at.%) ions and constant Ho3+ (1 at.%) and Bi3+ (2 at.%) concentrations were prepared. The sol-gel method with glycine as a fuel and citric acid as a chelator was chosen for sample preparation. All samples were heated in the furnace for 1.5 h at 500 °C and then thermally treated for 2.5 h at 1000 °C. The pure orthorhombic lattice of SrGd2O4, space group Pnma, was revealed by X-ray diffraction (XRD) (JCPDS Card No.:01-072-6387). Transmission electron microscopy (TEM) discovered agglomerated clusters of spherical particles measuring around 150 nm in size. Including Bi3+ ions into the structure influenced the morphology of the sample showing fine packing of pyramidal-shaped nanoparticles. The uniform distribution of constitutive elements in the samples was confirmed by energy dispersive spectroscopy (EDS). Up-conversion emission properties were evaluated from photoluminescent emission spectra and intensity dependence on excitation power after excitation at 976 nm. Dominant green (550 nm), red (671 nm), and infrared (758 nm) 5F4, 5S2 → 5I8, 5F5 → 5I8, 5F4, 5S2 → 5I7 transition emissions, respectively, are detected in all samples. The sample co-doped with Bi3+ showed the most intense photoluminescent emission.
PB  - Belgrade : Institut za multidisciplinarna istraživanja
C3  - Programme and the Book of Abstracts / 7th Conference of The Serbian Society for Ceramic Materials, 7CSCS-2023, June 14-16, 2023 Belgrade, Serbia
T1  - Enhancement of up-conversion luminescent characteristics of Yb3+/Ho3+ co-doped Bi3+ based SrGd2O4 nanoparticles
UR  - https://hdl.handle.net/21.15107/rcub_dais_14663
ER  - 

@conference{
author = "Stamenković, Tijana and Radmilović, Nadežda and Dinić, Ivana and Vuković, Marina and Barudžija, Tanja and Čebela, Maria and Lojpur, Vesna",
year = "2023",
abstract = "In this investigation, samples of SrGd2O4 doped with different Yb3+ (2, 4, 6 at.%) ions and constant Ho3+ (1 at.%) and Bi3+ (2 at.%) concentrations were prepared. The sol-gel method with glycine as a fuel and citric acid as a chelator was chosen for sample preparation. All samples were heated in the furnace for 1.5 h at 500 °C and then thermally treated for 2.5 h at 1000 °C. The pure orthorhombic lattice of SrGd2O4, space group Pnma, was revealed by X-ray diffraction (XRD) (JCPDS Card No.:01-072-6387). Transmission electron microscopy (TEM) discovered agglomerated clusters of spherical particles measuring around 150 nm in size. Including Bi3+ ions into the structure influenced the morphology of the sample showing fine packing of pyramidal-shaped nanoparticles. The uniform distribution of constitutive elements in the samples was confirmed by energy dispersive spectroscopy (EDS). Up-conversion emission properties were evaluated from photoluminescent emission spectra and intensity dependence on excitation power after excitation at 976 nm. Dominant green (550 nm), red (671 nm), and infrared (758 nm) 5F4, 5S2 → 5I8, 5F5 → 5I8, 5F4, 5S2 → 5I7 transition emissions, respectively, are detected in all samples. The sample co-doped with Bi3+ showed the most intense photoluminescent emission.",
publisher = "Belgrade : Institut za multidisciplinarna istraživanja",
journal = "Programme and the Book of Abstracts / 7th Conference of The Serbian Society for Ceramic Materials, 7CSCS-2023, June 14-16, 2023 Belgrade, Serbia",
title = "Enhancement of up-conversion luminescent characteristics of Yb3+/Ho3+ co-doped Bi3+ based SrGd2O4 nanoparticles",
url = "https://hdl.handle.net/21.15107/rcub_dais_14663"
}

Stamenković, T., Radmilović, N., Dinić, I., Vuković, M., Barudžija, T., Čebela, M.,& Lojpur, V.. (2023). Enhancement of up-conversion luminescent characteristics of Yb3+/Ho3+ co-doped Bi3+ based SrGd2O4 nanoparticles. in Programme and the Book of Abstracts / 7th Conference of The Serbian Society for Ceramic Materials, 7CSCS-2023, June 14-16, 2023 Belgrade, Serbia
Belgrade : Institut za multidisciplinarna istraživanja..
https://hdl.handle.net/21.15107/rcub_dais_14663

Stamenković T, Radmilović N, Dinić I, Vuković M, Barudžija T, Čebela M, Lojpur V. Enhancement of up-conversion luminescent characteristics of Yb3+/Ho3+ co-doped Bi3+ based SrGd2O4 nanoparticles. in Programme and the Book of Abstracts / 7th Conference of The Serbian Society for Ceramic Materials, 7CSCS-2023, June 14-16, 2023 Belgrade, Serbia. 2023;.
https://hdl.handle.net/21.15107/rcub_dais_14663 .

Stamenković, Tijana, Radmilović, Nadežda, Dinić, Ivana, Vuković, Marina, Barudžija, Tanja, Čebela, Maria, Lojpur, Vesna, "Enhancement of up-conversion luminescent characteristics of Yb3+/Ho3+ co-doped Bi3+ based SrGd2O4 nanoparticles" in Programme and the Book of Abstracts / 7th Conference of The Serbian Society for Ceramic Materials, 7CSCS-2023, June 14-16, 2023 Belgrade, Serbia (2023),
https://hdl.handle.net/21.15107/rcub_dais_14663 .

TY  - JOUR
AU  - Stamenković, Tijana
AU  - Dinić, Ivana
AU  - Vuković, Marina
AU  - Radmilović, Nadežda
AU  - Barudžija, Tanja
AU  - Tomić, Miloš
AU  - Mančić, Lidija
AU  - Lojpur, Vesna
PY  - 2023
UR  - http://cherry.chem.bg.ac.rs/handle/123456789/6087
AB  - In this investigation, samples of strontium-gadolinium-oxide (SrGd2O4) doped with different Yb3+ (2, 4 and 6 at%) and constant Ho3+ (1 at%) contents and co-doped with Bi3+ (2 at%) were prepared using the glycine-assisted sol–gel method. The pure orthorhombic SrGd2O4 phase, space group Pnma, was revealed using X-ray diffraction in all samples. Transmission electron microscopy discovered agglomerated clusters of spherical particles measuring approximately 150 nm in size. The inclusion of Bi3+ ions into the structure influenced the morphology since the formation of larger grains was observed, with sizes reaching up to ∼1.7 μm. The uniform distribution of all constitutive elements was confirmed by energy-dispersive X-ray spectroscopy. In all samples, up-conversion emission spectra revealed two dominant green (540 and 550 nm), red (671 nm), and infrared (758 nm) emission lines, due to the 5F4,5S2→5I8, 5F5→5I8, and 5F4,5S2 → 5I7 transitions, respectively. The sample co-doped with Bi3+ showed the most intense photoluminescent emissions, shorter luminescence decay, and the highest quantum yield. Additionally, a significant decrease in the energy band gap value was detected using diffuse reflectance spectroscopy for this sample. Methylene blue was used as a test pollutant to investigate its photocatalytic efficiency under simulated sunlight irradiation. The results show that Bi3+ co-doping deteriorates the photocatalytic efficiency of the SrGd2O4:Yb3+/Ho3+ phase by reducing hydroxyl radical formation.
PB  - Elsevier
T2  - Ceramics International
T1  - Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase
VL  - 49
IS  - 23
SP  - 37758
EP  - 37767
DO  - 10.1016/j.ceramint.2023.09.103
UR  - https://hdl.handle.net/21.15107/rcub_dais_15138
ER  - 

@article{
author = "Stamenković, Tijana and Dinić, Ivana and Vuković, Marina and Radmilović, Nadežda and Barudžija, Tanja and Tomić, Miloš and Mančić, Lidija and Lojpur, Vesna",
year = "2023",
abstract = "In this investigation, samples of strontium-gadolinium-oxide (SrGd2O4) doped with different Yb3+ (2, 4 and 6 at%) and constant Ho3+ (1 at%) contents and co-doped with Bi3+ (2 at%) were prepared using the glycine-assisted sol–gel method. The pure orthorhombic SrGd2O4 phase, space group Pnma, was revealed using X-ray diffraction in all samples. Transmission electron microscopy discovered agglomerated clusters of spherical particles measuring approximately 150 nm in size. The inclusion of Bi3+ ions into the structure influenced the morphology since the formation of larger grains was observed, with sizes reaching up to ∼1.7 μm. The uniform distribution of all constitutive elements was confirmed by energy-dispersive X-ray spectroscopy. In all samples, up-conversion emission spectra revealed two dominant green (540 and 550 nm), red (671 nm), and infrared (758 nm) emission lines, due to the 5F4,5S2→5I8, 5F5→5I8, and 5F4,5S2 → 5I7 transitions, respectively. The sample co-doped with Bi3+ showed the most intense photoluminescent emissions, shorter luminescence decay, and the highest quantum yield. Additionally, a significant decrease in the energy band gap value was detected using diffuse reflectance spectroscopy for this sample. Methylene blue was used as a test pollutant to investigate its photocatalytic efficiency under simulated sunlight irradiation. The results show that Bi3+ co-doping deteriorates the photocatalytic efficiency of the SrGd2O4:Yb3+/Ho3+ phase by reducing hydroxyl radical formation.",
publisher = "Elsevier",
journal = "Ceramics International",
title = "Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase",
volume = "49",
number = "23",
pages = "37758-37767",
doi = "10.1016/j.ceramint.2023.09.103",
url = "https://hdl.handle.net/21.15107/rcub_dais_15138"
}

Stamenković, T., Dinić, I., Vuković, M., Radmilović, N., Barudžija, T., Tomić, M., Mančić, L.,& Lojpur, V.. (2023). Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase. in Ceramics International
Elsevier., 49(23), 37758-37767.
https://doi.org/10.1016/j.ceramint.2023.09.103
https://hdl.handle.net/21.15107/rcub_dais_15138

Stamenković T, Dinić I, Vuković M, Radmilović N, Barudžija T, Tomić M, Mančić L, Lojpur V. Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase. in Ceramics International. 2023;49(23):37758-37767.
doi:10.1016/j.ceramint.2023.09.103
https://hdl.handle.net/21.15107/rcub_dais_15138 .

Stamenković, Tijana, Dinić, Ivana, Vuković, Marina, Radmilović, Nadežda, Barudžija, Tanja, Tomić, Miloš, Mančić, Lidija, Lojpur, Vesna, "Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase" in Ceramics International, 49, no. 23 (2023):37758-37767,
https://doi.org/10.1016/j.ceramint.2023.09.103 .,
https://hdl.handle.net/21.15107/rcub_dais_15138 .